Bending Aluminum Sheet 6061

But the question remains the same which alloy is the best product for bending.

Bending aluminum sheet 6061. What about the 6061t6 aluminum plate bending 90 degrees compared to the 3000 series and 5000 series. 1 32 in. Recommended minimum bend radii for 90 degree cold forming of sheet plate temper 1 64 in. From non heat treatable 3003 and 5052 to the heat treatable 2024 6061 and 7075 you have many options from which to choose.

Will 6061t6 aluminum plate will be cracked at 90 degrees. 3 16 in. That is it gets stronger and harder by working bending it. This site should not be used to determine if a.

In my 40 plus years in the trade i have bent quite a lot of 6061 t6 aluminum. The general purpose 6061 aluminum sheet plate is heat treatable resists cracking due to stress and is easy to weld and machine but limited on formability. When you are forming aluminum if the radius is sharp small in relation to the material thickness you will overwork the material making it harder more brittle and much more likely to fail. 3 8 in.

6061 aluminum sheet plate are ideal for structural framing base plates gussetts aircraft marine and automotive parts etc. This is generalizing as there are ways to bend 6061 but for general bending you use 3003 or 5052 grain direction bend line should go across the grain for the best bend having said that a typical sharp 90 bend on a piece of 1 8 aluminum sheet should be a minimum 1 8 inside radius use either 3003 or 5052 ideally the bend line should go. Clinton aluminum offers a variety of products each covering a wide range of applications and processes. O 0 0 0 1t 1t 1t 1 1 2 t 2t.

Aluminum minimum bend radii for 90 degree cold forming of sheet and plate. The data provided on our website has been vetted to the best of our availabilities. 1 4 in. Chances are that you ll never make it to 90 degrees much less make it to an external angle of 100 degrees.

Per the aluminum association inc. Aluminum where necessary 5052 h32 may be bent to 1t and 6061 t6 to 1 1 2t. Just like all sheet metal aluminum work hardens during the forming process. 1 8 in.

When you are bending 0 25 in thick 6061 t6 cracking can occur when bending past an external angle of just 86 degrees. To our valued customers. 1 2 in.